納米碳酸鈣增強聚丙烯纖維的研究

編號：SLHY00048

篇名：納米碳酸鈣增強聚丙烯纖維的研究

作者：鄭楠; 高緒珊; 童儼;

關(guān)鍵詞：聚丙烯纖維; 碳酸鈣; 納米; 分散劑; 力學(xué)性能; 結(jié)構(gòu);

機構(gòu)： 北京服裝學(xué)院; 北京服裝學(xué)院 北京;

摘要： 將分散劑、納米碳酸鈣和聚丙烯(PP)切片按一定比例混合紡絲制得改性PP纖維。并研究了改性PP纖維的結(jié)構(gòu)與性能。結(jié)果表明:當分散劑與納米碳酸鈣的質(zhì)量比為1∶3,納米碳酸鈣質(zhì)量分數(shù)為0．3%時,改性PP纖維的斷裂強度和初始模量最大,分別為7．97,90．36 cN/dtex．納米碳酸鈣在改性PP纖維中分散均勻,且粒徑為40～80 nm。與PP纖維相比,改性PP纖維的取向度變化不大,結(jié)晶度有所提高,但當納米碳酸鈣質(zhì)量分數(shù)大于等于2%時,其結(jié)晶度下降明顯。 The modified PP fiber was prepared by blending a dispersant,nano-calcium carbonate and polypropylene(PP) chips at a specific ratio.The structure and properties of modified PP fiber were studied.The results showed that the breaking strength and initial modulus were maximized as 7.79 and 90.36 cN/dtex respectively when the mass ratio of the dispersant to nano-calcium carbonate was 1∶3 and the content of nano-calcium carbonate was 0.3% by mass fraction.The nano-calcium car- bonate with particle size of 40-80μm...